Loctite® Fixmaster® Steel Putty, 2-Part, EA 3471, 1 lb

Description

Loctite® Fixmaster® Steel Putty, 2-Part, Series: EA 3471, Tub Container, 1 lb Container, Epoxy Base, Composition: Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenediphenol, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine, Paste Form, 278 sq-cm at 6 mm THK/0.45 kg Coverage, 30 min Application Time, 6 hr Curing, Gray/White, Part A: Slight/Musty, Part B: Ammoniacal Odor/Scent, -30 to 105 deg C, Part A: 2.6/Part B: 1.5 Specific Gravity, >93 deg C Flash Point, 2.5:1 By Volume/6.25:1 By Weight Mixing Ratio, <10 g/L VOC, Applicable Materials: Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum, 4900 psi Tensile Strength, 1395 psi Shear Strength

Features:

• Steel putty is a non-slumping, two-part, steel-filled putty
• Will not sag or shrink
• Rebuilds worn parts fast limits downtime
• High steel content cures to a metal-like finish
• Superior adhesion bonds well to all metal substrates
• D 85 shore hardness
• 35 to 40 gel time at 21 deg C
• Epoxy resin part A, epoxy hardener part B

Applications:

Filling Mild Steel and Forming Molds

Standards/Approval:

• ABS Approved
• CFIA Approved
• ISO Certified
• NAVSEA
• NEHC
• OSHA 29 CFR 1910.1200
• GHS Certified

Applicable Materials	Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum
Application Time	30 min
Base Type	Epoxy
Color	Gray/White
Composition	Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenediphenol, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine
Container Size	1 lb
Container Type	Tub
Coverage	278 sq-cm at 6 mm THK/0.45 kg
Curing Time	6 hr
Flash Point	>93 deg C
Form	Paste
Mixing Ratio	2.5:1 By Volume/6.25:1 By Weight
Odor/Scent	Part A: Slight/Musty, Part B: Ammoniacal
Series	EA 3471
Shear Strength	1395 psi
Specific Gravity	Part A: 2.6/Part B: 1.5
Temperature Rating	-30 to 105 deg C
Manufacturer	Loctite®