Loctite® Fixmaster® Putty, 8 oz, Steel, 30 min Cure Time

Description

Loctite® Fixmaster® Putty, 1-Part, Can Container, 8 oz Container, Water Base, Composition: Steel, Silicic Acid, Potassium Salt, Paste Form, 620 sq-cm at 0.25 cm THK/0.45 kg Coverage, 30 min Application Time, 5 to 7 hr Curing, Silver, Odorless Odor/Scent, 2000 deg F, 1.54 Specific Gravity, Applicable Materials: Cast Aluminum, Cast Iron, Carbon Steel, 675 psi Shear Strength

Features:

• Putty is a fluid, self-leveling aluminum liquid
• Can be poured into molds and cavities
• Makes reliable high temperature repairs
• One part design, no mixing, no measuring
• Cures to a metal finish
• Can be ground and sanded to a smooth finish
• For casting aluminum replacement parts and for making molds,

Applications:

Boiler Doors and Casings, Exhaust Stacks, Defective Molds, Crucibles and Dies, Flanges, Sagger Plates, Refractory Bricks and Ceramic Tiles, Automotive Exhaust Application: Headers, Manifolds, Catalytic Converters and Exhaust Ports

Standards/Approval:

• ABS Approved
• RoHS 2011/65/EU
• OSHA 29 CFR 1910.1200
• GHS Certified

Applicable Materials	Cast Aluminum, Cast Iron, Carbon Steel
Application Time	30 min
Base Type	Water
Color	Silver
Composition	Steel, Silicic Acid, Potassium Salt
Container Size	8 oz
Container Type	Can
Coverage	620 sq-cm at 0.25 cm THK/0.45 kg
Curing Time	5 to 7 hr
Form	Paste
Odor/Scent	Odorless
Shear Strength	675 psi
Specific Gravity	1.54
Temperature Rating	2000 deg F
Type	1-Part
Manufacturer	Loctite®