KSCdirect Part #: LOC 235613
Description: LOCTITE EA 3476 1LBEN (97443)
MFG Part #: 235613
UPC: 079340974432
Supplier: LOCTITE CORPORATION
Usually ships in 10 days.
You will be notified of any delay and may cancel at that time.

Your Price: $152.78 / EA

QTY:  
For shipping rates, add item to cart.
* Quantity discounts may be available. Call Kelly Supply at 800-918-8939.
Alternatively, you may e-mail info@kscdirect.com for service.

Details

Description

Loctite® Fixmaster® Stainless Steel Putty, 2-Part, Series: EA 3476, Tub Container, 1 lb Container, Epoxy Base, Composition: Part A: Calcium Carbonate, Epoxy Polyamine Adduct, Amine Adduct, Triethylenetetramine, Diethylenetriamine Silica Filler, Nonylphenol, Titanium Dioxide, 4-Methylimidazole, Part B: Epoxy Resin Chromium, Nickel, Molybdenum, Paste Form, 232 sq-cm at 6 mm THK/0.45 kg Coverage, 20 min Application Time, 6 hr Curing, Dark/Blue/Gray Part A, Gray Part B, Part A: Amine, Part B: Mild Odor/Scent, 30 to 105 deg C, Part A: 1.57/Part B: 3.832 Specific Gravity, Part A: > 93 deg C, Part B: 149 deg C Flash Point, 4:1, 9:1 Mixing Ratio, <10 g/L VOC, Applicable Materials: Steel, Cast Iron, Stainless Steel, Concrete, Wood, Clean, Abraded Bronze, Copper, Aluminum, 4600 psi Tensile Strength, 1800 psi Shear Strength

Features:

  • Resists rust and corrosion for long lasting repairs
  • Rebuilds worn parts fast limits downtime
  • High stainless steel content for durability
  • Superior adhesion forms a solid bond
  • Non-sag putty allows application versatility by conforming to unusual shapes
  • D 85 shore hardness
  • 40 to 50 min gel time 25 deg C
  • Epoxy hardener part A, epoxy resin part B

Standards/Approval:

  • ABS Approved
  • CFIA Approved
  • ISO Certified
  • NAVSEA
  • NEHC
  • OSHA 29 CFR 1910.1200
  • GHS Certified

Attributes/Specifications

Applicable Materials Steel, Cast Iron, Stainless Steel, Concrete, Wood, Clean, Abraded Bronze, Copper, Aluminum
Application Time 20 min
Base Type Epoxy
Color Dark/Blue/Gray Part A, Gray Part B
Composition Part A: Calcium Carbonate, Epoxy Polyamine Adduct, Amine Adduct, Triethylenetetramine, Diethylenetriamine Silica Filler, Nonylphenol, Titanium Dioxide, 4-Methylimidazole, Part B: Epoxy Resin Chromium, Nickel, Molybdenum
Container Size 1 lb
Container Type Tub
Coverage 232 sq-cm at 6 mm THK/0.45 kg
Curing Time 6 hr
Flash Point Part A: > 93 deg C, Part B: 149 deg C
Form Paste
Mixing Ratio 4:1, 9:1
Odor/Scent Part A: Amine, Part B: Mild
Series EA 3476
Shear Strength 1800 psi
Specific Gravity Part A: 1.57/Part B: 3.832
Temperature Rating 30 to 105 deg C
Manufacturer LOCTITE CORPORATION