Description

Loctite® Fixmaster® Wear Resistant Putty, 2-Part, Series: PC 7222, Kit Container, 3 lb Container, Epoxy Base, Composition: Part A: Aluminum Oxide, Diethylenetriamine, Alkyl Phenol, Silicon Dioxide, Epoxy Polyamine Adduct, 4,4'-Isopropylidenediphenol, Triethylenetetramine, Substituted Piperazine, Titanium Dioxide, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Silicon Carbide, Epoxy Resin, Aluminum Oxide, Treated Fumed Silica, Cristobalite, Carbon Black, Aluminum, Paste Part A/Solid/Paste Part B Form, 342 sq-cm at 6 mm THK/0.45 kg Coverage, 30 min Application Time, 6 hr Curing, Dark Gray Part A, Gray Part B, Part A: Ammoniacal, Part B: Slight/Epoxy Odor/Scent, -30 to 105 deg C, Part A: 1.07/Part B: 2.228 Specific Gravity, Part A: > 93 deg C, Part B: 250 deg C Flash Point, 2:1 By Volume/2:1 By Weight Mixing Ratio, Applicable Materials: Aluminum, Brass, Concrete, Iron, Plastic, Steel, Wood, 3020 psi Tensile Strength, 2440 psi Shear Strength

Features:

• Ceramic fibers that give this trowelable putty excellent wear and abrasion resistant properties under typical dry service temperatures of -29 to 107 deg C
• Provides smooth, low friction finish for equipment exposed to wear, erosion, and cavitation
• Renews worn surfaces fast reduces downtime
• Small ceramic bead filled resists fine particle sliding abrasion, prolongs equipment life
• D 89 shore hardness
• 45 to 55 gel time at 25 deg C
• Epoxy hardener part A, epoxy resin part B

Applications:

Abrasion Resistant, Corrosion Protection, Wear Resistant Coatings and Wear-Resistant Coatings

Standards/Approval:

• ABS Approved
• CFIA Approved
• ISO Certified
• NAVSEA
• NEHC
• OSHA 29 CFR 1910.1200
• GHS Certified

Applicable Materials	Aluminum, Brass, Concrete, Iron, Plastic, Steel, Wood
Application Time	30 min
Base Type	Epoxy
Color	Dark Gray Part A, Gray Part B
Composition	Part A: Aluminum Oxide, Diethylenetriamine, Alkyl Phenol, Silicon Dioxide, Epoxy Polyamine Adduct, 4,4'-Isopropylidenediphenol, Triethylenetetramine, Substituted Piperazine, Titanium Dioxide, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Silicon Carbide, Epoxy Resin, Aluminum Oxide, Treated Fumed Silica, Cristobalite, Carbon Black, Aluminum
Container Size	3 lb
Container Type	Kit
Coverage	342 sq-cm at 6 mm THK/0.45 kg
Curing Time	6 hr
Flash Point	Part A: > 93 deg C, Part B: 250 deg C
Form	Paste Part A/Solid/Paste Part B
Mixing Ratio	2:1 By Volume/2:1 By Weight
Odor/Scent	Part A: Ammoniacal, Part B: Slight/Epoxy
Series	PC 7222
Shear Strength	2440 psi
Specific Gravity	Part A: 1.07/Part B: 2.228
Temperature Rating	-30 to 105 deg C
Manufacturer	LOCTITE CORPORATION